Case Hardening Steels

170.00 - 390.00 INR

Get a Price/Quote

Product Details:

Material Composition % C: 0.15-0.25%, Mn: 0.5-1.0%, Cr: 0.5-1.4%, Ni: 1.0-3.5% (typical by grade)
Tensile Strength 600-850 MPa (varies by grade)
Heat Resistance Yes
Hardness Up to 62 HRC (after case hardening)
Recyclable Yes
Size Custom sizes as per order
Product Form Bars, Rounds, Flats, Plates
Click to View more

Request to Call Back Send Inquiry

Product Details
Product Description

Case Hardening Steels Price And Quantity

Price Range 170.00 - 390.00 INR
Minimum Order Quantity 100 Kilograms

Delivery Condition Annealed/Normalized/Pre-machined
Lead Time 2-4 weeks
Packing Standard export-worthy packing
Machinability Good prior to hardening
Process Type Carburising, Nitriding, Induction Hardening
Minimum Order Quantity 1 Ton/As per client requirement
Case Hardening Depth 0.5 to 2.5 mm (as per process)
Availability Ready stock & custom production
Elongation 10-14% (varies with grade)
Impact Strength High (for core toughness)

Case Hardening Steels Product Specifications

Composition Varies by grade: Carbon, Manganese, Chromium, Nickel
Application Hard-wearing surface applications, gears, automotive components, shafts
Dimension (L*W*H) As per requirement
Thickness Custom sizes available
Surface Bright/Black
Material Composition % C: 0.15-0.25%, Mn: 0.5-1.0%, Cr: 0.5-1.4%, Ni: 1.0-3.5% (typical by grade)
Tensile Strength 600-850 MPa (varies by grade)
Grade EN-353, EN-36C, 20MnCr5, 16MnCr5, SAE8620, 15NiCr13
Steel Product Type Industrial Steel Plates, Bars, Rounds
Steel Standard ASTM, AISI, EN, DIN, JIS
Heat Resistance Yes
Product Name Case Hardening Steels
Weight Custom/Varies
Finish Type Bright, Black, Ground, Rough
Usage Engineering, Automotive, Heavy Equipment
Size Custom sizes as per order
Shape Round, Square, Flat
Hardness Up to 62 HRC (after case hardening)
Steel Type Alloy Steel
Recyclable Yes
Material Grade Case Hardening Grades
Product Form Bars, Rounds, Flats, Plates
Color Metallic Grey
Corrosion Resistant Medium (can be improved with surface treatments)
Coating Type None/As per customer demand
Diameter 6 mm to 600 mm

Delivery Condition Annealed/Normalized/Pre-machined
Lead Time 2-4 weeks
Packing Standard export-worthy packing
Machinability Good prior to hardening
Process Type Carburising, Nitriding, Induction Hardening
Minimum Order Quantity 1 Ton/As per client requirement
Case Hardening Depth 0.5 to 2.5 mm (as per process)
Availability Ready stock & custom production
Elongation 10-14% (varies with grade)
Impact Strength High (for core toughness)

Case Hardening Steels Trade Information

Supply Ability 100000 Kilograms Per Week
Delivery Time 1-7 Days

Product Description

Case Hardening Steels

Case Hardening Steels offered by us, are those steels which are known for wear resistant surfaces and high core toughness. These steels are very effective and great to use for hardening. These steels is well known for fracture resistance under load conditions. These steels are very easy to install and simple to use. Case Hardening Steels are mainly used for engineered components too. These steels are very cost effective and can be easily availed by our eminent customers, in bulk quantities.

Engineered for Durability and Performance

Case Hardening Steels provide an optimal balance between surface hardness (up to 62 HRC post-hardening) and a resilient inner core. Their tailored chemical composition enhances resistance to wear, mechanical stress, and surface fatigue, making them ideal for gears, shafts, and components exposed to demanding operating conditions.

Versatile Case Hardening Processes

Utilizing carburising, nitriding, or induction hardening, the case depth and properties can be adapted as per application needs. Each process ensures optimal surface characteristics while maintaining core integrity and machinability before hardening, offering design flexibility for engineers.

Custom Sizing and Delivery

With custom dimensioning (length, width, height, and thickness), and multiple shapesround, square, or flatCase Hardening Steels can be manufactured as per client requirements. Export-grade packing and prompt delivery help meet project timelines efficiently across various industry sectors.

FAQs of Case Hardening Steels:

Q: How are Case Hardening Steels processed to achieve surface hardness?

A: Case Hardening Steels undergo processes like carburising, nitriding, or induction hardening. These methods introduce hardening elements to the steels surface, creating a wear-resistant outer layer (0.5 to 2.5 mm deep) while preserving a tough, ductile core for enhanced performance in demanding applications.

Q: What applications typically use Case Hardening Steels?

A: These steels are commonly employed for hard-wearing surface applications such as gears, automotive components, shafts, and parts of heavy equipment where a combination of surface hardness and core toughness is crucial for durability and reliability.

Q: When is case hardening recommended for steel components?

A: Case hardening is recommended when a component needs a hard, wear-resistant surface to reduce abrasion or surface fatigue, while maintaining internal toughness to absorb shocks. This approach is suitable before final machining or after the initial shaping of parts.

Q: Where are these steels manufactured and supplied from?

A: Case Hardening Steels are manufactured, exported, and supplied by leading distributors, exporters, and manufacturers in India. They are available for both domestic and international markets, with export-worthy packaging to ensure safe delivery.

Q: What are the benefits of using case hardening processes for alloy steels?

A: The primary benefit is the enhanced surface hardness (up to 62 HRC) for excellent wear resistance, while the core remains tough and impact-resistant. This dual structure significantly extends the service life of parts subjected to both high loads and friction.

Q: How does machinability of Case Hardening Steels compare prior to hardening?

A: These steels offer good machinability in the annealed, normalized, or pre-machined delivery condition, allowing complex parts to be easily manufactured prior to undergoing the hardening process.

Q: What order quantities and lead times are possible for Case Hardening Steels?

A: Minimum order quantities start at 1 ton or as per client requirement. With both ready stock and custom production available, typical lead times range from 2 to 4 weeks depending on order size and customization needs.

Tell us about your requirement

Price:

Quantity

Select Unit

50
100
200
250
500
1000+

Additional detail

Mobile number

Other Products in 'High Steel Product' category

Nitriding Steel Price Range : 170.00 - 390.00 INR Minimum Order Quantity : 100 Diameter : 10 mm to 400 mm Color : Silver metallic gray Coating Type : Nitrided surface layer (typically 0.30.7 mm case depth) Corrosion Resistant : Moderate (improved after surface treatment/nitriding) Material Grade : Nitriding Quality Alloy Steel Recyclable : Yes Product Form : Hot Rolled, Forged, Peeled, Turned, Polished Shape : Other, Round, Flat, Square, Hex, and Custom Profiles Steel Type : Alloy Steel Hardness : Surface hardness up to 68 HRC after nitriding Finish Type : Polished, Black, as per requirement Size : Standard/Custom lengths up to 6 meters Usage : Ideal for highly stressed parts requiring high fatigue and wear resistance Heat Resistance : Yes Product Name : Other, Nitriding Steel Weight : Variable depending on size and form Tensile Strength : 800 1100 MPa (varies by grade and heat treatment) Grade : EN41B, EN40B, DIN 1.8509, AISI 4140, AISI 4150 and other custom nitriding grades Steel Product Type : Other, Bars, Rods, Flats, and Custom Shapes Steel Standard : Other, ASTM, DIN, JIS, BS, IS (as per customer requirements) Dimension (L*W*H) : Customizable as per clients requirement Application : Other, Used for manufacturing gears, crankshafts, camshafts, valve parts, piston rods, injection mold tooling, and other engine components requiring high surface hardness and wear resistance. Composition : Basic composition includes Chromium, Aluminum, Molybdenum, with Carbon and other alloying elements as per specific grade Material Composition % : Cr: 1.01.5%, Al: 0.81.1%, Mo: 0.150.3% (varies by grade) Thickness : Available from 10 mm to 200 mm Surface : Annealed / Peeled / Polished / Black / Bright

Send Inquiry

High Speed Steel Bar Price Range : 170.00 - 390.00 INR Minimum Order Quantity : 100 Diameter : 6 mm to 100 mm or customized Color : Metallic Grey Coating Type : Uncoated / Available with TiN or TiAlN coating on request Corrosion Resistant : Moderate Material Grade : M2, M35, M42 Recyclable : Yes Product Form : Bar Shape : Other, Round, Flat, Square Steel Type : Other, High Speed Steel (HSS) Hardness : 6267 HRC (depends on grade and heat treatment) Finish Type : Bright, Ground, or Black Size : Standard and custom sizes available Usage : Manufacturing of drills, taps, end mills, cutters, saw blades Heat Resistance : Yes Product Name : Other, High Speed Steel Bar Weight : Depends on dimensions and length Tensile Strength : Between 9001200 MPa (varies by grade) Grade : M2, M35, M42 (other grades available on request) Steel Product Type : Other, Flat Bar / Round Bar Steel Standard : Other, AISI, DIN, JIS, ASTM Dimension (L*W*H) : Customized as per requirement Application : Other, Cutting tools, dies, punches, and machine tool components Composition : W, Mo, V, Co, Cr, C in varying proportions depending on grade Material Composition % : C: 0.81.5%, W: 5.519%, Mo: 4.510%, V: 1.84%, Co (if present): 48%, Cr: 3.84.5% Thickness : Varies, typically from 2 mm to 80 mm Surface : Bright / Black / Ground Finish

Send Inquiry

High Speed Steel Rod Price Range : 170.00 - 390.00 INR Minimum Order Quantity : 100 Diameter : 6mm to 80mm Color : Silver, Metallic Grey Coating Type : Uncoated or as specified (optional: TiN, TiCN, etc.) Corrosion Resistant : Moderate Material Grade : Available in multiple grades (M2, M35, M42, etc.) Recyclable : Yes Product Form : Rod Shape : Other, Round Steel Type : Other, High Speed Steel (HSS) Hardness : 6067 HRC (Heat Treated) Finish Type : Bright / Polished Size : Customizable, Standard sizes available Usage : Cutting tools, drills, taps, reamers, punches, industrial applications Heat Resistance : Yes Product Name : Other, High Speed Steel Rod Weight : Depends on size and length Tensile Strength : Approx. 9001200 MPa (varies by grade) Grade : M2, M35, M42 or as per requirement Steel Product Type : Other, Round Rod Steel Standard : Other, AISI, ASTM, DIN, JIS, EN Standards Dimension (L*W*H) : DIA 6MM TO 80MM, LENGTH 100MM TO 6000MM Application : Other, Automobile Industry, Manufacturing, Tool Making, Construction, Engineering, Cutting Tools Composition : Tungsten, Molybdenum, Chromium, Vanadium, Cobalt, Carbon, Iron Material Composition % : Varies by grade, e.g., W: 56.5%, Mo: 4.55.5%, Cr: 3.54.5%, V: 1.52.2%, C: 0.81.1%, Co (optional): 4.58% Thickness : 6mm to 80mm (Diameter) Surface : Bright, Polished Finish